ASTM A588 STEEL STEEL SPECIFICATION
| Epesè | Lajè | Longè |
|---|---|---|
| 5 a 150 mm | 900 a 4800 mm | 3000 a 12000 mm |
| Spesifikasyon | Koupe | Egalize |
| ASTM A588 | flanm, waterjet, plasma, lazè | Klas A, B, K |
Tablo gwosè nan plak Corten A588
| Fòma | Lajè | Epesè | Longè |
|---|---|---|---|
| Cho woule (moulen teren) | 48″, 60″, 72″ | 3/16″ – 1/2″ | Nenpòt |
| Koupe longè | 84″, 96″ | 3/16″ – 1/2″ | Nenpòt |
| Bobi | 48″, 60″, 72″, 84″, 96″ | 3/16″ – 1/2″ | Nenpòt |
| Disrè (moulen woule) | 96″ | 48″, 60″, 72″ | 240″ – 480″ |
A588 Steel Fèy Pwopriyete mekanik
| Klas A | Cr | Mn | P | C | S | Si | NI | CO | V |
|---|---|---|---|---|---|---|---|---|---|
| 0.40-0.65% | 0.80 – 1.25% | 0.030% | 0.19% | 0.030% | 0.03 – 0.65% | 0.40% | 0.25-0.40% | 0.02-0.10% | |
| Klas B | 0.40-0.70% | 0.75 – 1.35% | 0.030% | 0.20% | 0.030% | 0.15 – 0.50% | 0.50% | 0.20-0.40% | 0.01-0.10% |
A588 Steel Fèy Pwopriyete mekanik
| Metrik | Enpeyal | |
|---|---|---|
| Fòs rupture, sede | 250 MPa | 36,300 psi |
| Fòs rupture, ultim | 400 - 550 MPa | 58,000 - 79,800 psi |
| Chea modil | 79.3 GPA | 11,500 ksi |
| Elongasyon nan kraze (nan 50 mm) | 23.0% | 23.0% |
| Elongasyon nan kraze (nan 200 mm) | 20.0% | 20.0% |
| Modil esansyèl (tipik pou asye) | 140 GPA | 20,300 ksi |
| Modil Elastisite | 200 GPA | 29,000 ksi |
| Poissons rapò | 0.260 | 0.260 |
A588 dezagregasyon ekivalan asye
| Lafrans Afnor | Ewòp en | Almay Din, WNR | Itali Uni | Angletè BS | Lachin GB | Larisi Gost |
|---|---|---|---|---|---|---|
| – | S355J2G1W | Wtst 52-3 | Fe 510 D2K1 | WR 50 C | – | – |
Diferans ki genyen ant ASTM A588 Klas B plak asye ak ASTM A588 Klas A plak asye
Konpozisyon chimik:ASTM A588 Klas A plak asye ak klas B plak asye gen diferan konpozisyon chimik. Klas A plak gen ladan apeprè 0.20-0.55% kwiv, pandan y ap klas B plak gen yon kontni kwiv ki pi wo nan sou 0.25-0.65%.
Anplis de sa, plak klas B ka gen yon ti kras pi wo nivo nan nikèl (Ni) ak CHROMIUM (CR). Varyasyon sa yo afekte rezistans korozyon plak yo ak pwopriyete mekanik yo.
Pwopriyete mekanik:Plak asye ASTM A588 Klas B montre yon fòs sede ki pi gran pase oswa egal a 345-450 MPa ak yon fòs rupture nan 485-620 MPa, tou de depase sa yo ki nan klas A plak asye (sede fòs pi gran pase oswa egal a 345 MPa, fòs rupture 485-620 MPA). Sa a endike plak B Klas yo ofri fòs siperyè ak severite anba pi lou charj.
Pèfòmans koube:Due to their higher strength characteristics, ASTM A588 Grade B plates typically require preheating for bending operations involving thicknesses >25mm oswa reyon Bend sere. Klas A plak, sepandan, mande pou ti kras oswa ki pa gen prechofe nan menm kondisyon yo, fè yo pi fasil yo fòme.
Aplikasyon:ASTM A588 Klas B plak asye, ak pi wo fòs li yo, se tipikman itilize nan aplikasyon pou estriktirèl mande siperyè pwopriyete mekanik ak rezistans chaj van, tankou pon (chvoch depase 100 mèt), segondè - monte eksteryè, ak gwo fò tou won.
ASTM A588 Klas APlak asye se pi souvan travay nan aplikasyon jeneral estriktirèl, ki gen ladan depo, limyè - estrikti devwa, ak ankadreman ekipman yo.
Li enpòtan pou note ke tou deASTM A588 Klas Aak plak asye klas B montre ekselan rezistans korozyon, reyisi yon endèks rezistans dezagregasyon ki gen plis pase oswa egal a 6.0 nan ASTM G101 tès, fè yo apwopriye pou anviwònman deyò oswa ekspoze.
Lè w ap chwazi nòt plak asye, desizyon yo ta dwe baze sou yon evalyasyon konplè sou kondisyon chaj pwojè a, epesè, pwosesis koube, ak kondisyon anviwònman an, pandan y ap konfòme yo avèk estanda ki enpòtan ak espesifikasyon.